Crossover from diffusive to tunneling regime in NbN/DyN/NbN ferromagnetic semiconductor tunnel junctions
Physical Review B
American Physical Society
MetadataShow full item record
Muduli, P., Pal, A., & Blamire, M. (2014). Crossover from diffusive to tunneling regime in NbN/DyN/NbN ferromagnetic semiconductor tunnel junctions. Physical Review B, 89 https://doi.org/10.1103/PhysRevB.89.094414
We have investigated NbN-DyN-NbN junctions with 1 to 10 nm thick DyN barriers. A crossover from diffusive (hopping) to tunneling-type transport was found in these junctions as the DyN thickness is reduced below ∼4 nm. We have also made a detailed study of magnetic and electrical properties of thicker DyN thin films deposited under similar conditions; DyN films were found to be ferromagnetic with TCurie∼35±5 K. Electrical transport of the junctions with ∼10 nm DyN was understood in terms of Shklovskii-Efros (SE)-type variable range hopping (VRH) at low temperature between 90 and 35 K. We estimated localization length ξ=5.6 nm in this temperature range. Temperature dependence of resistance was found to deviate from SE-VRH below 35 K along with large suppression of resistance with magnetic field. This is correlated with onset of magnetism below 35 K. Large butterfly-shaped MR up to ∼40% was found for the ∼10 nm thick DyN junction at 2 K. In the tunneling regime, barrier height of the tunnel junction was estimated ∼50 meV from the Simmons model. Signatures of spin filtering was found in temperature dependence of resistance in tunnel junction with ∼3 nm thick DyN. Cooper pair tunneling in these junctions below TC (∼10.8 K) of NbN was understood according to S-I-S tunneling current model. We found coherent tunneling of Cooper pairs through a ∼1 nm thick DyN tunnel barrier with critical current IC∼12 μA. The critical current also showed modulation with magnetic field.
This work was supported by the ERC Advanced Investigator Grant SUPERSPIN.
External DOI: https://doi.org/10.1103/PhysRevB.89.094414
This record's URL: https://www.repository.cam.ac.uk/handle/1810/245214