Effect of Y-211 particle size on the growth of single grain Y–Ba–Cu–O bulk superconductors
Journal of Crystal Growth
MetadataShow full item record
Thoma, M., Shi, Y., Dennis, T., Durrell, J., & Cardwell, D. (2014). Effect of Y-211 particle size on the growth of single grain Y–Ba–Cu–O bulk superconductors. Journal of Crystal Growth, 412 31-39. https://doi.org/10.1016/j.jcrysgro.2014.11.037
The engineering of fine Y2Ba1Cu1O5 (Y-211) inclusions of average particle size 1−2 μm within the continuous, superconducting YBa2Cu3O7−δ (Y-123) phase matrix of single-grain, bulk high temperature Y–Ba–Cu–O (YBCO) superconductors is fundamental to achieving high critical current density in these materials. However, bulk samples fabricated using fine Y-211 precursor powders generally suffer from incomplete growth of the Y-123 phase compared to samples fabricated with coarser Y-211 particles of average particle size >5 μm in the precursor powder. In this study, the effects of Y-211 particle size on processing parameters during growth of large single YBCO grains are reported. Chemical analysis using EDX of cross-sections of single YBCO grains indicates that the loss of liquid phase during melt processing is greater when finer Y-211 precursor powder is employed, which accounts for the observed growth limitations and low sample yield. Specific modifications to the single grain growth process have been made based on the results of this investigation to reduce liquid loss and to enable the use of fine Y-211 precursor powder without compromising complete single grain growth or yield.
A1. Fine Y-211 particle size, A1. Liquid loss, A2. Heating profile, A2. YBCO single grain growth
Yunhua Shi would thank the financial support from EPSRC (grant ref. EP/K02910X/1), United Kingdom.
External DOI: https://doi.org/10.1016/j.jcrysgro.2014.11.037
This record's URL: https://www.repository.cam.ac.uk/handle/1810/246844
Attribution 2.0 UK: England & Wales
Licence URL: http://creativecommons.org/licenses/by/2.0/uk/
Recommended or similar items
The following licence files are associated with this item: