The effect of magnesium on the local structure and initial dissolution rate of simplified UK Magnox waste glasses
Journal of Non-Crystalline Solids
MetadataShow full item record
Guo, R., Brigden, C., Gin, S., Swanton, S., & Farnan, I. (2018). The effect of magnesium on the local structure and initial dissolution rate of simplified UK Magnox waste glasses. Journal of Non-Crystalline Solids, 497 82-92. https://doi.org/10.1016/j.jnoncrysol.2018.03.002
A series of simplified glasses were prepared to mimic the United Kingdom’'s Magnox radioactive waste glasses and determine the separate effect of the presence of Mg on the glass structure and the initial dissolution rate. These glasses had an alkaline earth (Ca/Mg) content of 6.5 mol% and relative ratios of Si, B and Na similar to 25 wt% waste loaded Magnox waste glass simulant. Each simplified glass had similar macroscopic properties, differing only in Ca/Mg ratio. 25Mg magic angle spinning nuclear magnetic resonance (MASNMR) spectra of the simplified Mg endmember (MgEM) glass (with no Ca) and the full-component simulant glass were similar, consistent with the similar Mg local environments in both glasses. 11B MASNMR spectra of the series of simplified glasses showed a systematic increase in the amount of three-coordinated boron (B) with increasing amounts of Mg. A clear change in the charge balancing of four-coordinated boron (B) by Mg compared with Ca is observed. However, 11B NMR measurements of the leached material showed that the additional B was not preferentially leached from the Mg containing samples. Despite the structural changes in the glass induced by Ca/Mg substitution, initial dissolution rates (r0) remained invariant, within error, with Ca/Mg ratio. This indicates that the poorer aqueous durability of Mg-containing Magnox waste glass measured experimentally in long-term leaching experiments, compared with SON68 glass containing Ca, is not caused by a primary structural effect in the glass.
R. Guo acknowledges the EPSRC and the University of Cambridge for an International Doctoral Scholarship. A portion of this work was funded by Radioactive Waste Management Limited (C.T. Brigden, S.W. Swanton and I. Farnan). The UK 850 MHz solid-state NMR Facility used in this research was funded by EPSRC and BBSRC (contract reference PR140003), as well as the University of Warwick including via part funding through Birmingham Science City Advanced Materials Projects 1 and 2 supported by Advantage West Midlands (AWM) and the European Regional Development Fund (ERDF). Collaborative assistance from the 850 MHz Facility Manager (Dinu Iuga, University of Warwick) is acknowledged.
Embargo Lift Date
External DOI: https://doi.org/10.1016/j.jnoncrysol.2018.03.002
This record's URL: https://www.repository.cam.ac.uk/handle/1810/275953
Attribution 4.0 International
Licence URL: http://creativecommons.org/licenses/by/4.0/
Recommended or similar items
The following licence files are associated with this item: