Ca Solubility in a BiFeO3-Based System with a Secondary Bi2O3 Phase on a Nanoscale.
Popov, Maxim N
J Phys Chem C Nanomater Interfaces
American Chemical Society (ACS)
MetadataShow full item record
Haselmann, U., Radlinger, T., Pei, W., Popov, M. N., Spitaler, T., Romaner, L., Ivanov, Y. P., et al. (2022). Ca Solubility in a BiFeO3-Based System with a Secondary Bi2O3 Phase on a Nanoscale.. J Phys Chem C Nanomater Interfaces https://doi.org/10.1021/acs.jpcc.2c00674
In BiFeO3 (BFO), Bi2O3 (BO) is a known secondary phase, which can appear under certain growth conditions. However, BO is not just an unwanted parasitic phase but can be used to create the super-tetragonal BFO phase in films on substrates, which would otherwise grow in the regular rhombohedral phase (R-phase). The super-tetragonal BFO phase has the advantage of a much larger ferroelectric polarization of 130-150 μC/cm2, which is around 1.5 times the value of the rhombohedral phase with 80-100 μC/cm2. Here, we report that the solubility of Ca, which is a common dopant of bismuth ferrite materials to tune their properties, is significantly lower in the secondary BO phase than in the observed R-phase BFO. Starting from the film growth, this leads to completely different Ca concentrations in the two phases. We show this with advanced analytical transmission electron microscopy techniques and confirm the experimental results with density functional theory (DFT) calculations. At the film's fabrication temperature, caused by different solubilities, about 50 times higher Ca concentration is expected in the BFO phase than in the secondary one. Depending on the cooling rate after fabrication, this can further increase since a larger Ca concentration difference is expected at lower temperatures. When fabricating functional devices using Ca doping and the secondary BO phase, the difference in solubility must be considered because, depending on the ratio of the BO phase, the Ca concentration in the BFO phase can become much higher than intended. This can be critical for the intended device functionality because the Ca concentration strongly influences and modifies the BFO properties.
External DOI: https://doi.org/10.1021/acs.jpcc.2c00674
This record's URL: https://www.repository.cam.ac.uk/handle/1810/338059
Attribution 4.0 International
Licence URL: https://creativecommons.org/licenses/by/4.0/
Recommended or similar items
The current recommendation prototype on the Apollo Repository will be turned off on 03 February 2023. Although the pilot has been fruitful for both parties, the service provider IKVA is focusing on horizon scanning products and so the recommender service can no longer be supported. We recognise the importance of recommender services in supporting research discovery and are evaluating offerings from other service providers. If you would like to offer feedback on this decision please contact us on: email@example.com