Role of the Secondary Phase η During High-Temperature Compression of ATI 718Plus®

Published version

Change log


Kienl, Christiane 
Mandal, Paranjayee 
Lalvani, Himanshu 
Rae, Catherine M. F. 


Abstract: High-temperature compression tests were performed on a Ni-base superalloy with a multi-phase microstructure. Particular attention was given on the influence of the η phase on recrystallization of ATI 718Plus®. The compression tests were performed at two temperatures over a variety of strains and strain rates. Meta-dynamic recrystallization was studied by exposing the samples to a set dwell time at the test temperature after deformation. Electron backscatter diffraction (EBSD) was used to investigate the microstructures after the tests. Secondary electron imaging (SEI) and scanning transmission electron microscopy (STEM) were utilized in order to investigate the deformation behavior of η and obtaining a detailed understanding of the recrystallization mechanism. The secondary η phase was found to increase the recrystallized fraction compared to η free tests. However, clusters of thin lamellar η inhibited recrystallization. The flow curve softening was distinctly stronger in the microstructure containing precipitates. It could be shown by SE images that this was due to the breakage and realignment of η. In addition, η was also found to accommodate the stresses by a remarkable deformation without breaking up. This was considered to be due to the composite nature of the precipitate as well as the ongoing recrystallization in the surrounding matrix.




Journal Title

Metallurgical and Materials Transactions A

Conference Name

Journal ISSN


Volume Title



Springer US