In situ observation of heat-induced degradation of perovskite solar cells
Di Carlo, A
Springer Science and Business Media LLC
MetadataShow full item record
Divitini, G., Cacovich, S., Matteocci, F., Cinà, L., Di Carlo, A., & Ducati, C. (2016). In situ observation of heat-induced degradation of perovskite solar cells. Nature Energy, 1 (15012) https://doi.org/10.1038/NENERGY.2015.12
The lack of thermal stability of perovskite solar cells is hindering the progress of this technology towards adoption in the consumer market. Different pathways of thermal degradation are activated at different temperatures in these complex nanostructured hybrid composites. Thus, it is essential to explore the thermal response of the mesosuperstructured composite device to engineer materials and operating protocols. Here we produce devices according to four well-established recipes, and characterize their photovoltaic performance as they are heated within the operational range. The devices are analysed using transmission electron microscopy as they are further heated in situ, to monitor changes in morphology and chemical composition. We identify mechanisms for structural and chemical changes, such as iodine and lead migration, which appear to be correlated to the synthesis conditions. In particular, we identify a correlation between exposure of the perovskite layer to air during processing and elemental diffusion during thermal treatment. Solar cells based on lead halide perovskite composites have become increasingly popular in the past few years owing to a combination of low synthesis cost and high power conversion efficiency, with certified values in excess of 20% (refs 1,2,3,4,5). However, the stability of such devices is a concern—it is well known that heating at or above around 85 ∘C, a temperature close to those reached during normal operation in full sunlight, performance degrades rapidly, and such instability is exacerbated by exposure to moisture; systematic thermal and ageing studies are required to understand such degradation processes. Changes happen in both the organic and inorganic components of the cells; the resilience of the perovskite layer, in particular, is expected to become a limiting factor once different hole-conducting materials (or hole-conductor-free cells) are developed. To overcome this limitation, it is vital to understand the degradation pathways of the structures involved, which here are observed at nanometre-scale spatial resolution in situ, inside an analytical scanning transmission electron microscope (STEM), while the composition is monitored with elemental mapping through energy-dispersive X-ray analysis (EDX). The analysis of such devices is challenging owing to several factors. The spatial dimensions relevant to the fabrication and the operation of the cells are in the 1–100 nm range, and the materials are easily damaged by exposure to an electron beam in a TEM, requiring careful tuning of the electron dose. The system also includes organic and inorganic components in an assembly with complex chemistry and morphology. Finally, the rapid changes to the devices in air and the low degradation temperatures pose an additional challenge to the experiment, which needs to be timed appropriately and carefully executed. The monitoring of this process is made possible by combining several recent advances in TEM technology. The use of high-brightness electron guns and detectors with large collection areas allows the fast acquisition of high-quality EDX maps with limited electron dose on the sample; the signal-to-noise ratio of the maps can be further increased by applying denoising algorithms (PCA, principal components analysis) within an open-source software suite. The development of novel in situ heating holders for TEM, based on micro-heaters and featuring high stability and fast response, was also crucial—in particular, the holder used here allows very precise control (sub-degree) at values just above room temperature, as well as providing fast heating and cooling (a few seconds for the temperatures in use in this paper). The good spatial stability of the holder is crucial in acquiring EDX maps.
G.D., S.C., and C.D. acknowledge funding from ERC under grant number 259619 PHOTO EM. C.D. acknowledges financial support from the EU under grant number 312483 ESTEEM2. F.M., L.C. and A.D.C. acknowledge funding from “Polo Solare Organico” Regione Lazio, the “DSSCX” MIURPRIN2010 and FP7 ITN “Destiny”. G.D and S.C. thank Dr. Francisco de la Peña and Dr. Pierre Burdet for assistance with PCA analysis.
European Research Council (259619)
European Commission (312483)
External DOI: https://doi.org/10.1038/NENERGY.2015.12
This record's URL: https://www.repository.cam.ac.uk/handle/1810/252676
Recommended or similar items
The current recommendation prototype on the Apollo Repository will be turned off on 03 February 2023. Although the pilot has been fruitful for both parties, the service provider IKVA is focusing on horizon scanning products and so the recommender service can no longer be supported. We recognise the importance of recommender services in supporting research discovery and are evaluating offerings from other service providers. If you would like to offer feedback on this decision please contact us on: firstname.lastname@example.org