Research data supporting 'Sample Dependence of Magnetism in the Next Generation Cathode Material LiNi0.8Mn0.1Co0.1O2'

Mukherjee, P., & Dutton, S. (2020). Research data supporting 'Sample Dependence of Magnetism in the Next Generation Cathode Material LiNi0.8Mn0.1Co0.1O2' [Dataset]. https://doi.org/10.17863/CAM.62029

Description

Contains data used to prepare all the figures in the publication. Fig. 1.cif contains the details of the crystal structure. Fig. 2 contains the X-ray and neutron diffraction refinement data. Figs 3, 4 and 5 contain the dc magnetic susceptibility, isothermal magnetisation and ac magnetic susceptibility data respectively. Fig. 6 contains the polarised neutron scattering data.

Format

Structural analysis was carried out using Fullprof. The crystal structure figure was prepared using vesta and all other figures were prepared using Origin.

Keywords

Diffraction, Neutron scattering, Rietveld refinement, Elemental analysis, Lithium ion battery cathode materials, Magnetic measurements

Relationships

Publication Reference: https://doi.org/10.1021/acs.inorgchem.0c02899 https://www.repository.cam.ac.uk/handle/1810/314989

Identifiers

This record's DOI: https://doi.org/10.17863/CAM.62029

Rights

Attribution 4.0 International, Attribution 4.0 International

Licence URL: http://creativecommons.org/licenses/by/4.0/http://creativecommons.org/licenses/by/4.0/

Except where otherwise noted, this item's licence is described as Attribution 4.0 International